Laser Etch Monitoring

From UCSB Nanofab Wiki
Revision as of 11:06, 9 September 2019 by John d (talk | contribs) (Monitoring Photoresist Etch Rate: minor caption formatting)
(diff) ← Older revision | Latest revision (diff) | Newer revision → (diff)
Jump to: navigation, search
Laser Etch Monitoring
Intellemetrics LEP500 Photo.jpg
Tool Type Dry Etch
Location ICP1, ICP2, Fluorine Etcher, DSE-iii
Supervisor Demis D. John
Supervisor Phone (805) 893-5934
Supervisor E-Mail demis@ucsb.edu
Description Laser Endpoint Detection for Dry Etching
Manufacturer Intellemetrics
Model LEP 500
Dry Etch Recipes


Overview

A number of our dry etching systems have Laser Etch monitors installed, for "endpoint detection". These systems allow you to end your etch at a known etch depth, or within a certain layer (with some caveats). This nearly eliminates the need to calibrate etch rates or to use timed etching only, which is especially important in our lab where etch rates can vary depending on the previous etches performed in the chamber.

Laser Etch monitoring works similarly to optical thin-film measurement via reflectivity spectra (eg. like our Filmetrics systems). However, instead of varying the optical wavelength and measuring a fixed thin-film, we measure a constant wavelength and a thin-film that is varying as it is etched. Thus, similar to the thin-film measurements, you can only measure a useful signal when the optical properties (reflection or interference) change during your etch.

For example, Etching from high-reflectivity Aluminum to Lower reflectivity Silicon will usually give you a clear drop showing that your Aluminum has been fully etched-through.

Etching films that are transparent at the laser monitor wavelength (670nm) produces a sinusoidal signal due to optical wave interference which gives you numerous possible stopping points to end the etch upon.

Procedures

General Procedure

The basic method for performing an etch with laser monitoring endpoint, is as follows:

  1. Simulate or estimate what the laser monitor trace will look like, decide when to stop the etch according to the laser monitor plot.
  2. Mount the sample such that the laser will be able to reach a region to monitor the etch - typically ~100-300µm wide area.
  3. Load sample into chamber - wafer transfer only, no etch.
  4. Align Laser onto area to monitor using co-axial microscope.
  5. Start laser power monitoring/logging.
  6. Start Etch (time set longer than expected etch time) - etch only, no wafer transfers.
    1. Closely observe laser monitor plot, comparing to known/simulated plot.
  7. Use "Next Step" or "End Step" when appropriate laser monitor trace is reached. Wait for process to complete any final steps.
  8. Transfer wafer out of chamber.
  9. Save laser monitor data, turn off laser & microscope illumination.

Specific Procedures

Procedures for specific machines are found on the following pages:

Examples

Monitoring Photoresist Etch Rate

Even if you don't use the laser monitor to determine when your etched material is removed, monitoring the photoresist mask alone is very helpful. For example, you can known exactly what time the photoresist is fully etched through during an etch (even if by accident), allowing you to stop the etch at that time, and still determine selectivity if desired.

example of photoresist monitor during etch.
Monitoring photoresist during two sequential etches: (1) ARC Etch (short O2 etch) from 100sec→120sec, and (2) subsequent Chromium etch (Cl2/O2) from 180sec until the etch completed at 500 sec. Plot shows that the photoresist survived - the sinusoid continued until the etch stopped, indicating that photoresist was still present and being etched.
annotated laser monitor plot of PR during a 3-step etch.
Monitoring the photoresist during a 3-step etch. Etch (1) Etches the Anti-Reflection underlayer (BARC) with O2, (2) etches Chromium with Cl2/O2 gases, and (3) intentionally etches the photoresist quickly with O2 to remove it fully. Manually Ended the step 30 sec after the plot showed the PR was fully removed, to account for any nonuniformity across the wafer.


References

See the following pages for more information about laser endpoint detection.